dental cad cam wieland zirconia blocks-3D multi layer high strength 600-1200Mpa


Share it


Multi layer wieland dental zirconia block hight strength

1,The multi layer dental zirconia block is for the open dental lab cad cam milling system:Wieland,Vhf,Roland etc

2,The high strength changes from 600 Mpa in incisal to 1200 Mpa in the cervix,which is perfect for the posterior.

3, The translucency changes from 49% at incisal to 40% at cervical,presenting a asethetic natural teeth.

4,Six layers of shade,strength,translucency are in nature transition,which is idear for final zirconia restoration.

5,With the 600-1200Mpa strength,it is designed for posterior with mul layer effect.It can be also application of veneer,implant,anterior crown and bridge.

5,Great aesthetic effect as original nature teeth.

3D high strength multi layer dental zirconia feature

Strength transition in 3D multilayer dental zirconia disc

flexural strength 3D multilayer dental zirconia specification


Indications: Crown, Inlay, Onlay, 2-6 unit Bridges,Anterior.


Sintered density:          6.07±0.01g/cm³
Bending Strength:        600-1200 MPa
Transmittance:             40-49%
Hardness:                       1250HV
Sintering temperature:    1480~1550℃/recommend 1500℃
Zirconia sintering chart

dental lab zirconia sintering chart

Additional information

Weight0.5 kg
Dimensions6 × 6 × 3 cm

10, 12, 14, 16, 18, 20, 22, 25


A1, A2, A3, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4


There are no reviews yet.

Be the first to review “dental cad cam wieland zirconia blocks-3D multi layer high strength 600-1200Mpa”

Your email address will not be published. Required fields are marked *

You may also like…